Multilayer Films and Laminates Containing Slip Agents

ABSTRACT

Provided is a coextruded multilayer film. The coextruded multilayer film has at least two layers, including a sealant layer and a second layer in contact with the sealant layer. The sealant layer contains (A) a first ethylene-based polymer having a density from 0.865 g/cc to 0.930 g/cc and a melt index from 0.5 g/10 min to 25 g/10 min; (B) an unsaturated primary fatty acid amide having a melting point of 100° C. or less; and (C) a diprotic fatty acid having a melting point greater than 100° C. and a decomposition temperature greater than 200° C. The second layer contains a second ethylene-based polymer. Also provided is a laminate containing said sealant layer.

BACKGROUND

The present disclosure relates to multilayer films and laminates havinga sealant layer containing an ethylene-based composition including slipagents.

Film layers formed from ethylene-based polymers are used in multilayerfilms for a variety of applications, including, for example, foodpackaging and specialty packaging. An ethylene-based polymer outer filmlayer requires a low coefficient of friction (COF) (e.g., less than0.30) for efficient processing of the films, such as in a fabricationline or a packaging line. To achieve a low COF, slip agents aretypically added to the ethylene-based polymer outer layer, which may bea sealant layer. Conventional slip agents include unsaturated fatty acidamides such as erucamide and oleamide, which are known to lower a film'sCOF by migrating to the surface of the film. However, it is difficult tomaintain a consistent low COF using conventional migratory slip agentsunder different environmental conditions, such as time, elevatedtemperature, elevated pressure, and various converting processes.Non-migratory slip agents such as silicones have also been added to theethylene-based polymer outer layer, but they are known to be lesseffective at achieving a low COF (e.g., less than 0.30). Additionally,non-migratory slip agents are more expensive than migratory slip agents.

The art recognizes the need for a film that includes an ethylene-basedpolymeric layer that exhibits a low COF (e.g., less than 0.30) without anon-migratory slip agent. The art also recognizes the need for alaminate that includes an ethylene-based polymeric layer that exhibits alow COF (e.g., less than 0.30) without a non-migratory slip agent.

SUMMARY

The present disclosure provides a coextruded multilayer film. Thecoextruded multilayer film contains at least two layers including asealant layer and a second layer in contact with the sealant layer. Thesealant layer contains (A) a first ethylene-based polymer having adensity from 0.865 g/cc to 0.930 g/cc and a melt index from 0.5 g/10 minto 25 g/10 min; (B) an unsaturated primary fatty acid amide having amelting point of 100° C. or less; and (C) a diprotic fatty acid having amelting point greater than 100° C. and a decomposition temperaturegreater than 200° C. The second layer contains a second ethylene-basedpolymer.

The present disclosure also provides a laminate. The laminate includes afirst film and a second film, wherein the first film is laminated to thesecond film. The first film includes a sealant layer containing (A) afirst ethylene-based polymer having a density from 0.865 g/cc to 0.930g/cc and a melt index from 0.5 g/10 min to 25 g/10 min; (B) anunsaturated primary fatty acid amide having a melting point of 100° C.or less; and (C) a diprotic fatty acid having a melting point greaterthan 100° C. and a decomposition temperature greater than 200° C.

Definitions

Any reference to the Periodic Table of Elements is that as published byCRC Press, Inc., 1990-1991. Reference to a group of elements in thistable is by the new notation for numbering groups.

For purposes of United States patent practice, the contents of anyreferenced patent, patent application or publication are incorporated byreference in their entirety (or its equivalent US version is soincorporated by reference) especially with respect to the disclosure ofdefinitions (to the extent not inconsistent with any definitionsspecifically provided in this disclosure) and general knowledge in theart.

The numerical ranges disclosed herein include all values from, andincluding, the lower and upper value. For ranges containing explicitvalues (e.g., 1 or 2, or 3 to 5, or 6, or 7), any subrange between anytwo explicit values is included (e.g., 1 to 2; 2 to 6; 5 to 7; 3 to 7; 5to 6; etc.).

Unless stated to the contrary, implicit from the context, or customaryin the art, all parts and percents are based on weight and all testmethods are current as of the filing date of this disclosure.

The term “alkyl” (or “alkyl moiety”), as described herein, refers to anorganic radical derived from an aliphatic hydrocarbon by deleting onehydrogen atom therefrom. An alkyl moiety may be linear, branched, cyclicor a combination thereof.

The terms “blend” or “polymer blend,” as used herein, is a blend of twoor more polymers. Such a blend may or may not be miscible (not phaseseparated at molecular level). Such a blend may or may not be phaseseparated. Such a blend may or may not contain one or more domainconfigurations, as determined from transmission electron spectroscopy,light scattering, x-ray scattering, and other methods known in the art.

The term “composition” refers to a mixture of materials which comprisethe composition, as well as reaction products and decomposition productsformed from the materials of the composition.

The terms “comprising,” “including,” “having” and their derivatives, arenot intended to exclude the presence of any additional component, stepor procedure, whether or not the same is specifically disclosed. Inorder to avoid any doubt, all compositions claimed through use of theterm “comprising” may include any additional additive, adjuvant, orcompound, whether polymeric or otherwise, unless stated to the contrary.In contrast, the term “consisting essentially of” excludes from thescope of any succeeding recitation any other component, step, orprocedure, excepting those that are not essential to operability. Theterm “consisting of” excludes any component, step, or procedure notspecifically delineated or listed. The term “or,” unless statedotherwise, refers to the listed members individually as well as in anycombination. Use of the singular includes use of the plural and viceversa.

An “ethylene-based polymer” is a polymer that contains more than 50weight percent polymerized ethylene monomer (based on the total amountof polymerizable monomers) and, optionally, may contain at least onecomonomer. Ethylene-based polymer includes ethylene homopolymer, andethylene copolymer (meaning units derived from ethylene and one or morecomonomers). The terms “ethylene-based polymer” and “polyethylene” maybe used interchangeably. Nonlimiting examples of ethylene-based polymer(polyethylene) include low density polyethylene (LDPE) and linearpolyethylene. Nonlimiting examples of linear polyethylene include linearlow density polyethylene (LLDPE), ultra low density polyethylene(ULDPE), very low density polyethylene (VLDPE), multi-componentethylene-based copolymer (EPE), ethylene/α-olefin multi-block copolymers(also known as olefin block copolymer (OBC)), single-site catalyzedlinear low density polyethylene (m-LLDPE), substantially linear, orlinear, plastomers/elastomers, and high density polyethylene (HDPE).Generally, polyethylene may be produced in gas-phase, fluidized bedreactors, liquid phase slurry process reactors, or liquid phase solutionprocess reactors, using a heterogeneous catalyst system, such asZiegler-Natta catalyst, a homogeneous catalyst system, comprising Group4 transition metals and ligand structures such as metallocene,non-metallocene metal-centered, heteroaryl, heterovalent aryloxyether,phosphinimine, and others. Combinations of heterogeneous and/orhomogeneous catalysts also may be used in either single reactor or dualreactor configurations. In an embodiment, the ethylene-based polymerdoes not contain an aromatic comonomer polymerized therein.

“Ethylene plastomers/elastomers” are substantially linear, or linear,ethylene/α-olefin copolymers containing homogeneous short-chainbranching distribution comprising units derived from ethylene and unitsderived from at least one C₃-C₁₀ α-olefin comonomer, or at least oneC₄-C₈ α-olefin comonomer, or at least one C₆-C₈ α-olefin comonomer.Ethylene plastomers/elastomers have a density from 0.870 g/cc, or 0.880g/cc, or 0.890 g/cc to 0.900 g/cc, or 0.902 g/cc, or 0.904 g/cc, or0.909 g/cc, or 0.910 g/cc, or 0.917 g/cc. Nonlimiting examples ofethylene plastomers/elastomers include AFFINITY™ plastomers andelastomers (available from The Dow Chemical Company), EXACT™ Plastomers(available from ExxonMobil Chemical), TafmerT™ (available from Mitsui),Nexlene™ (available from SK Chemicals Co.), and Lucene™ (available LGChem Ltd.).

A “fatty acid” is a carboxylic acid having a hydrocarbon chain and aterminal carboxyl group. The fatty acid may contain more than onecarboxyl group (e.g., a dicarboxyl fatty acid that contains two carboxylgroups).

“High density polyethylene” (or “HDPE”) is an ethylene homopolymer or anethylene/α-olefin copolymer with at least one C₄-C₁₀ α-olefin comonomer,or C₄₋C₈ α-olefin comonomer and a density from greater than 0.94 g/cc,or 0.945 g/cc, or 0.95 g/cc, or 0.955 g/cc to 0.96 g/cc, or 0.97 g/cc,or 0.98 g/cc. The HDPE can be a monomodal copolymer or a multimodalcopolymer. A “monomodal ethylene copolymer” is an ethylene/C₄-C₁₀α-olefin copolymer that has one distinct peak in a gel permeationchromatography (GPC) showing the molecular weight distribution. A“multimodal ethylene copolymer” is an ethylene/G₄-C₁₀ α-olefin copolymerthat has at least two distinct peaks in a GPC showing the molecularweight distribution. Multimodal includes copolymer having two peaks(bimodal) as well as copolymer having more than two peaks. Nonlimitingexamples of HDPE include DOW™ High Density Polyethylene (HDPE) Resins(available from The Dow Chemical Company), ELITE™ Enhanced PolyethyleneResins (available from The Dow Chemical Company), CONTINUUM™ BimodalPolyethylene Resins (available from The Dow Chemical Company), LUPOLEN™(available from LyondellBasell), as well as HDPE products from Borealis,Ineos, and Exxon Mobil.

A “hydrocarbon” is a compound that contains only hydrogen and carbonatoms. The hydrocarbon can be (i) branched or unbranched, (ii) saturatedor unsaturated (iii) cyclic or acyclic, and (iv) any combination of(i)-(iii). Nonlimiting examples of hydrocarbons include alkanes,alkenes, and alkynes.

An “interpolymer” is a polymer prepared by the polymerization of atleast two different monomers. This generic term includes copolymers,usually employed to refer to polymers prepared from two differentmonomers, and polymers prepared from more than two different monomers,e.g., terpolymers, tetrapolymers, etc.

“Low density polyethylene” (or “LDPE”) consists of ethylene homopolymer,or ethylene/α-olefin copolymer comprising at least one C₃-C₁₀ α-olefin,preferably C₃-C₄ that has a density from 0.915 g/cc to 0.940 g/cc andcontains long chain branching with broad MWD. LDPE is typically producedby way of high pressure free radical polymerization (tubular reactor orautoclave with free radical initiator). Nonlimiting examples of LDPEinclude MarFlex™ (Chevron Phillips), LUPOLEN™ (LyondellBasell), as wellas LDPE products from Borealis, Ineos, ExxonMobil, and others.

“Linear low density polyethylene” (or “LLDPE”) is a linearethylene/α-olefin copolymer containing heterogeneous short-chainbranching distribution comprising units derived from ethylene and unitsderived from at least one C₃-C₁₀ α-olefin comonomer or at least oneC₄-C₈ α-olefin comonomer, or at least one C₆-C₈ α-olefin comonomer.LLDPE is characterized by little, if any, long chain branching, incontrast to conventional LDPE. LLDPE has a density from 0.910 g/cc, or0.915 g/cc, or 0.920 g/cc, or 0.925 g/cc to 0.930 g/cc, or 0.935 g/cc,or 0.940 g/cc. Nonlimiting examples of LLDPE include TUFLINT™ linear lowdensity polyethylene resins (available from The Dow Chemical Company),DOWLEX™ polyethylene resins (available from the Dow Chemical Company),and MARLEX™ polyethylene (available from Chevron Phillips).

“Multi-component ethylene-based copolymer” (or “EPE”) comprises unitsderived from ethylene and units derived from at least one C₃-C₁₀α-olefin comonomer, or at least one C₄-C₈ α-olefin comonomer, or atleast one C₆-C₈ α-olefin comonomer, such as described in patentreferences U.S. Pat. Nos. 6,111,023; 5,677,383; and 6,984,695. EPEresins have a density from 0.905 g/cc, or 0.908 g/cc, or 0.912 g/cc, or0.920 g/cc to 0.926 g/cc, or 0.929 g/cc, or 0.940 g/cc, or 0.962 g/cc.Nonlimiting examples of EPE resins include ELITE′ enhanced polyethylene(available from The Dow Chemical Company), ELITE AT™ advanced technologyresins (available from The Dow Chemical Company), SURPASS™ Polyethylene(PE) Resins (available from Nova Chemicals), and SMARTT™ (available fromSK Chemicals Co.).

An “olefin-based polymer” or “polyolefin” is a polymer that containsmore than 50 weight percent polymerized olefin monomer (based on totalamount of polymerizable monomers), and optionally, may contain at leastone comonomer. Nonlimiting examples of an olefin-based polymer includeethylene-based polymer and propylene-based polymer.

A “polymer” is a compound prepared by polymerizing monomers, whether ofthe same or a different type, that in polymerized form provide themultiple and/or repeating “units” or “mer units” that make up a polymer.The generic term polymer thus embraces the term homopolymer, usuallyemployed to refer to polymers prepared from only one type of monomer,and the term copolymer, usually employed to refer to polymers preparedfrom at least two types of monomers. It also embraces all forms ofcopolymer, e.g., random, block, etc. The terms “ethylene/α-olefinpolymer” and “propylene/α-olefin polymer” are indicative of copolymer asdescribed above prepared from polymerizing ethylene or propylenerespectively and one or more additional, polymerizable α-olefin monomer.It is noted that although a polymer is often referred to as being “madeof” one or more specified monomers, “based on” a specified monomer ormonomer type, “containing” a specified monomer content, or the like, inthis context the term “monomer” is understood to be referring to thepolymerized remnant of the specified monomer and not to theunpolymerized species. In general, polymers herein are referred to hasbeing based on “units” that are the polymerized form of a correspondingmonomer.

A “propylene-based polymer” is a polymer that contains more than 50weight percent polymerized propylene monomer (based on the total amountof polymerizable monomers) and, optionally, may contain at least onecomonomer.

“Single-site catalyzed linear low density polyethylenes” (or “m-LLDPE”)are linear ethylene/α-olefin copolymers containing homogeneousshort-chain branching distribution comprising units derived fromethylene and units derived from at least one C₃-C₁₀ α-olefin comonomer,or at least one C₄-C₈ α-olefin comonomer, or at least one C₆-C₈ α-olefincomonomer. m-LLDPE has density from 0.913 g/cc, or 0.918 g/cc, or 0.920g/cc to 0.925 g/cc, or 0.940 g/cc. Nonlimiting examples of m-LLDPEinclude EXCEED™ metallocene PE (available from ExxonMobil Chemical),LUFLEXEN™ m-LLDPE (available from LyondellBasell), and ELTEX™ PF m-LLDPE(available from Ineos Olefins & Polymers).

“Ultra low density polyethylene” (or “ULDPE”) and “very low densitypolyethylene” (or “VLDPE”) each is a linear ethylene/α-olefin copolymercontaining heterogeneous short-chain branching distribution comprisingunits derived from ethylene and units derived from at least one C₃-C₁₀α-olefin comonomer, or at least one C₄-C₈ α-olefin comonomer, or atleast one C₆-C₈ α-olefin comonomer. ULDPE and VLDPE each has a densityfrom 0.885 g/cc, or 0.90 g/cc to 0.915 g/cc. Nonlimiting examples ofULDPE and VLDPE include ATTANE™ ULDPE resins (available form The DowChemical Company) and FLEXOMER™ VLDPE resins (available from The DowChemical Company).

Test Methods

Coefficient of Friction (COF) is measured according to ASTM D1894. TheCOF is measured as a film-to-film dynamic COF using a substrate filmcontaining DOWLEX™ 2045G and 1000 ppm erucamide, fixed to a GM-1 COFTester from Guangzhou Biaoji Packaging Instrument Co. Ltd. COF ismeasured at room temperature (25° C.) and 35% relative humidity. COF ismeasured in the machine direction at a sliding speed of 100 millimetersper minute. “Pre-Lamination COF” is measured on a film sample that isnot laminated. “Laminate COF” is measured on a laminate structure aftercuring at 60° C. for 60 hours.

The “decomposition temperature” is the temperature at which the diproticfatty acid chemically decomposes (i.e., one or more chemical bondsbreak). Decomposition temperature is measured by placing 20 mg of asample in a platinum pan before being introduced into the carrousel of aTGA Q500 instrument. The sample is heated in a nitrogen/air atmosphereat a rate of 10° C./min from room temperature (25° C.) to 700° C. TAsoftware reports the decomposition temperature.

Density is measured in accordance with ASTM D792, Method B. The resultis recorded in grams per cubic centimeter (g/cc).

Melt index (MI) (12) in g/10 min is measured using ASTM D-1238-04 (190°C./2.16 kg).

Differential Scanning Calorimetry (DSC)

Differential Scanning calorimetry (DSC) can be used to measure themelting, crystallization, and glass transition behavior of a polymerover a wide range of temperature. For example, the TA Instruments 01000DSC, equipped with an RCS (refrigerated cooling system) and anautosampler is used to perform this analysis. During testing, a nitrogenpurge gas flow of 50 ml/min is used. Each sample is melt pressed into athin film at 190° C.; the melted sample is then air-cooled to roomtemperature (25° C.). A 3-10 mg, 6 mm diameter specimen is extractedfrom the cooled polymer, weighed, placed in a light aluminum pan (50mg), and crimped shut. Analysis is then performed to determine itsthermal properties.

The thermal behavior of the sample is determined by ramping the sampletemperature up and down to create a heat flow versus temperatureprofile. First, the sample is rapidly heated to 180° C. and heldisothermal for 3 minutes in order to remove its thermal history. Next,the sample is cooled to −80° C. at a 10° C./minute cooling rate and heldisothermal at −80° C. for 3 minutes. The sample is then heated to 180°C. (this is the “second heat” ramp) at a 10° C./minute heating rate. Thecooling and second heating curves are recorded. The values determinedare extrapolated onset of melting, Tm, and extrapolated onset ofcrystallization, Tc. Heat of fusion (Hf) (in Joules per gram), thecalculated % crystallinity for polyethylene samples using the followingequation: % Crystallinity ═((Hf)/292 J/g)×100; and the calculated %crystallinity for polyethylene samples using the following equation: %Crystallinity=((Hf)/292 J/g)×100. The heat of fusion (Hf) and the peakmelting temperature are reported from the second heat curve. Peakcrystallization temperature is determined from the cooling curve.

Melting point, Tm, is determined from the DSC heating curve by firstdrawing the baseline between the start and end of the meltingtransition. A tangent line is then drawn to the data on the lowtemperature side of the melting peak. Where this line intersects thebaseline is the extrapolated onset of melting (Tm). This is as describedin Bernhard Wunderlich, The Basis of Thermal Analysis, in ThermalCharacterization of Polymeric Materials 92, 277-278 (Edith A. Turi ed.,2d ed. 1997).

DETAILED DESCRIPTION

The present disclosure provides a coextruded multilayer film. Thecoextruded multilayer film has at least two layers, including a sealantlayer and a second layer in contact with the sealant layer. The sealantlayer contains (A) a first ethylene-based polymer having a density from0.865 g/cc to 0.930 g/cc and a melt index from 0.5 g/10 min to 25 g/10min; (B) an unsaturated primary fatty acid amide having a melting pointof 100° C. or less; and (C) a diprotic fatty acid having a melting pointgreater than 100° C. and a decomposition temperature greater than 200°C. The second layer contains a second ethylene-based polymer.

The multilayer film contains two layers, or more than two layers. Forexample, the multilayer film can have two, three, four, five, six,seven, eight, nine, ten, eleven, or more layers. In an embodiment, themultilayer film contains only two layers, or only three layers.

1. Sealant Layer

The coextruded multilayer film contains a sealant layer. The sealantlayer contains (A) a first ethylene-based polymer having a density from0.865 g/cc to 0.930 g/cc and a melt index from 0.5 g/10 min to 25 g/10min; (B) an unsaturated primary fatty acid amide having a melting pointof 100° C. or less; (C) a diprotic fatty acid having a melting pointgreater than 100° C. and a decomposition temperature greater than 200°C.; (D), optionally, a saturated primary fatty acid amide having amelting point greater than 100° C.; and (E) optionally, an additive.

The sealant layer has two opposing surfaces. In an embodiment, thesealant layer is a continuous layer with two opposing surfaces.

A. First Ethylene-Based Polymer

The sealant layer contains a first ethylene-based polymer. Theethylene-based polymer has a density from 0.865 g/cc to 0.930 g/cc and amelt index from 0.5 g/10 min to 25 g/10 min. Nonlimiting examples ofsuitable ethylene-based polymer include LDPE and linear polyethylene.Nonlimiting examples of linear polyethylene include LLDPE, ULDPE, VLDPE,EPE, ethylene/α-olefin multi-block copolymers (also known as OBC),m-LLDPE, substantially linear, or linear, plastomers/elastomers, andcombinations thereof. Nonlimiting examples of suitable ethylene-basedpolymer also include ethylene/α-olefin interpolymer andethylene/α-olefin copolymer. Nonlimiting examples of suitable α-olefinsinclude C₃-C₂₀ α-olefins, or C₄-C₂₀ α-olefins, or C₃-C₁₀ α-olefins, orC₄-C₁₀ α-olefins, or C₄-C₈ α-olefins. Representative α-olefins includepropylene, 1-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene. In anembodiment, the ethylene-based polymer is an ethylene/1-octeneinterpolymer.

In an embodiment, the ethylene-based polymer contains greater than 50 wt% units derived from ethylene, or from 51 wt %, or 55 wt %, or 60 wt %to 70 wt %, or 80 wt %, or 90 wt %, or 95 wt %, or 99 wt %, or 100 wt %units derived from ethylene; and a reciprocal amount of units derivedfrom an α-olefin comonomer, or from less than 50 wt %, or 49 wt %, or 45wt %, or 40 wt % to 30 wt %, or 20 wt %, or 10 wt %, or 5 wt %, or 1 wt%, or 0 wt % units derived from an α-olefin comonomer, based on theweight of the ethylene-based polymer.

The ethylene-based polymer has a density from 0.865 g/cc, or 0.870 g/cc,or 0.875 g/cc, or 0.880 g/cc, or 0.885 g/cc, or 0.890 g/cc, or 0.895g/cc, or 0.900 g/cc, or 0.910 g/cc, or 0.915 g/cc to 0.920 g/cc, or0.925 g/cc, or 0.930 g/cc.

The ethylene-based polymer has a melt index from 0.5 g/10 min, or 1.0g/10 min to 1.5 g/10 min, or 2.0 g/10 min, or 3.0 g/10 min, or 4.0 g/10min, or 5.0 g/10 min, or 8.0 g/10 min, or 10 g/10 min, or 15 g/10 min,or 20 g/10 min, or 25 g/10 min.

In an embodiment, the ethylene-based polymer is a LLDPE. The LLDPE is anethylene homopolymer or an ethylene/α-olefin copolymer consisting ofunits derived from ethylene and a C₃-C₁₀ α-olefin comonomer, or a C₄-C₈α-olefin comonomer, or a C₆-C₈ α-olefin comonomer. In an embodiment, theLLDPE has density from 0.910 g/cc, or 0.915 g/cc, or 0.920 g/cc to 0.925g/cc, or 0.930 g/cc; and a melt index from 0.5 g/10 min, or 1.0 g/10 minto 1.5 g/10 min, or 2.0 g/10 min, or 3.0 g/10 min, or 4.0 g/10 min, or5.0 g/10 min, or 8.0 g/10 min, or 10 g/10 min, or 15 g/10 min, or 20g/10 min, or 25 g/10 min. In an embodiment, the ethylene-based polymeris a LLDPE that is an ethylene/1-octene copolymer.

In an embodiment, the ethylene-based polymer is a LDPE. The LDPE is anethylene homopolymer or an ethylene/α-olefin copolymer consisting ofunits derived from ethylene and a C₃-C₁₀ α-olefin comonomer, or a C₄-C₈α-olefin comonomer, or a C₆-C₈ α-olefin comonomer. In an embodiment, theLDPE has density from 0.915 g/cc, 0.916 g/cc to 0.918 g/cc, or 0.920g/cc, or 0.925 g/cc, or 0.930 g/cc; and a melt index from 0.5 g/10 min,or 1.0 g/10 min, or 1.5 g/10 min, or 2.0 g/10 min, or 3.0 g/10 min, or4.0 g/10 min, or 5.0 g/10 min, or 8.0 g/10 min to 10 g/10 min, or 11g/10 min, or 15 g/10 min, or 20 g/10 min, or 25 g/10 min.

The sealant layer may contain more than one ethylene-based polymer. Inan embodiment, the sealant layer includes at least two ethylene-basedpolymers, wherein each ethylene-based polymer differs from one anothercompositionally, structurally, and/or physically. For example, thesealant layer may contain an LLDPE and a LDPE.

In an embodiment, the sealant layer contains from 70 wt %, or 75 wt %,or 80 wt %, or 85 wt %, or 90 wt % to 93 wt %, or 94 wt %, or 95 wt %,or 98 wt %, or 99 wt %, or 99.5 wt %, or 99.99 wt % ethylene-basedpolymer, based on the total weight of the sealant layer. In anotherembodiment, the sealant layer contains from 94 wt %, or 95 wt %, or 99wt % to 99.99 wt % ethylene-based polymer, based on the total weight ofthe sealant layer.

In an embodiment, the ethylene-based polymer is selected from LLDPE,LDPE, and combinations thereof.

The ethylene-based polymer may comprise two or more embodimentsdisclosed herein.

B. Unsaturated Primary Fatty Acid Amide

The sealant layer contains an unsaturated primary fatty acid amidehaving a melting point of 100° C. or less. An “unsaturated primary fattyacid amide” is a molecule having the Structure (I):

wherein R is a C₃ to C₂₄ alkyl moiety that is mono-unsaturated orpoly-unsaturated. In an embodiment, R is a C₁₁ to C₂₄, or a C₁₅ to C₂₃alkyl moiety, or a C₁₇ to C₂₁ alkyl moiety that is mono-unsaturated orpoly-unsaturated. A “mono-unsaturated” alky moiety is an alkyl that hasone double bond (a C═C bond), with all of the remainder carbon atomsbeing linked via single bonds (C—C bonds). A “poly-unsaturated” alkymoiety is an alkyl that has at least two double bonds (C═C bonds). In anembodiment, R is selected from a C₁₇ alkyl moiety and a C₂₁ alkyl moietythat is mono-unsaturated or poly-unsaturated. In an embodiment, R ismono-unsaturated. Nonlimiting examples of suitable unsaturated primaryfatty acid amides include erucamide, oleamide, and combinations thereof.

In an embodiment, in the unsaturated primary fatty acid amide of theStructure (I), R is a C₂₁ alkyl moiety that is mono-unsaturated. In afurther embodiment, the unsaturated primary fatty acid amide iserucamide. Erucamide has the following Structure (II):

In an embodiment, in the unsaturated primary fatty acid amide of theStructure (I), R is a C₁₇ alkyl moiety that is mono-unsaturated. In afurther embodiment, the unsaturated primary fatty acid amide isoleamide. Oleamide has the following Structure (III):

The unsaturated primary fatty acid amide has a melting point of 100° C.or less. In an embodiment, the unsaturated primary fatty acid amide hasa melting point from 40° C., or 50° C., or 60° C., or 65° C., or 70° C.,or 75° C. to 80° C., or 85° C., or 90° C., or 95° C., or 100° C. In anembodiment, the unsaturated primary fatty acid amide is erucamide, whichhas a melting point of 75° C.-80° C. In another embodiment, theunsaturated primary fatty acid amide is oleamide, which has a meltingpoint of 70° C.

The sealant layer may contain more than one unsaturated primary fattyacid amide. In an embodiment, the sealant layer includes at least twounsaturated primary fatty acid amides, wherein each unsaturated primaryfatty acid amide differs from one another compositionally, structurally,and/or physically.

In an embodiment, the sealant layer contains from 0.00047 wt % (4.7parts per million (ppm)), or 0.001 wt % (10 ppm), or 0.0095 wt % (95ppm), or 0.01 wt % (100 ppm), or 0.05 wt % (500 ppm) to 0.08 wt % (800ppm), or 0.10 wt % (1000 ppm), or 0.20 wt % (2000 ppm), or 0.24 wt %(2400 ppm), or 0.5 wt % (5000 ppm), or 1.0 wt % (10000 ppm), or 2.0 wt %(20000 ppm), or 3.0 wt % (30000 ppm), or 4.0 wt % (40000 ppm), or 4.5 wt% (45000 ppm), or 4.76 wt % (47600 ppm) unsaturated primary fatty acidamide, based on the total weight of the sealant layer.

The unsaturated primary fatty acid amide may comprise two or moreembodiments disclosed herein.

C. Diprotic Fatty Acid

The sealant layer contains a diprotic fatty acid having a melting pointgreater than 100° C. and a decomposition temperature greater than 200°C. A “diprotic fatty acid” is a fatty acid having two ionizable hydrogenatoms per molecule. A nonlimiting example of a suitable diprotic fattyacid is a dicarboxyl fatty acid. In an embodiment, the diprotic fattyacid is a dicarboxyl fatty acid. Nonlimiting examples of suitabledicarboxyl fatty acids include succinic acid, hexanedioic acid,octanedioic acid, decanedioic acid, and dodecanedioic acid. In anembodiment, the diprotic fatty acid is selected from succinic acid(C₄H₆O₄), hexanedioic acid (C₆H₁₀O₄), octanedioic acid (C₈H₁₄O₄),decanedioic acid (C₁₀H₁₈O₄), dodecanedioic acid (C₁₂H₂₂O₄), andcombinations thereof. In an embodiment, the diprotic fatty acid containsfrom 4 to 6, or 8, or 10, or 12, or 14, or 16, or 20 carbon atoms.

The diprotic fatty acid has a melting point greater than 100° C. In anembodiment, the diprotic fatty acid has a melting point from greaterthan 100° C. to 250° C., or from 101° C., or 105° C., or 110° C., or120° C., or 130° C., or 140° C., or 150° C., or 160° C., or 170° C., or180° C. to 185° C., or 190° C., or 200° C., or 210° C., or 220° C., or230° C., or 240° C., or 250° C.

The diprotic fatty acid has a decomposition temperature greater than200° C. In an embodiment, the diprotic fatty acid has a decompositiontemperature from greater than 200° C. to 500° C., or from 201° C., or205° C., or 210° C., or 220° C., or 225° C., or 230° C., or 235° C. to240° C., or 245° C., or 250° C., or 270° C., or 300° C., or 310° C., or320° C., or 330° C., or 340° C., or 350° C., or 380° C., or 400° C., or450° C., or 500° C.

In an embodiment, the diprotic fatty acid is succinic acid, which has amelting point of 184° C. and a decomposition temperature of 235° C.Succinic acid has the following Structure (IV):

In an embodiment, the sealant layer contains from 0.00047 wt % (4.7ppm), or 0.001 wt % (10 ppm), or 0.0095 wt % (95 ppm), or 0.01 wt % (100ppm), or 0.02 wt % (200 ppm) to 0.05 wt % (500 ppm), or 0.10 wt % (1000ppm), or 0.20 wt % (2000 ppm), or 0.24 wt % (2400 ppm), or 0.5 wt %(5000 ppm), or 1.0 wt % (10000 ppm), or 2.0 wt % (20000 ppm), or 3.0 wt% (30000 ppm), or 4.0 wt % (40000 ppm), or 4.5 wt % (45000 ppm), or 4.76wt % (47600 ppm) diprotic fatty acid, based on the total weight of thesealant layer.

The sealant layer may contain more than one diprotic fatty acid. In anembodiment, the sealant layer includes at least two diprotic fattyacids, wherein each diprotic fatty acid differs from one anothercompositionally, structurally, and/or physically.

The diprotic fatty acid may comprise two or more embodiments disclosedherein.

D. Optional Saturated Primary Fatty Acid Amide

In an embodiment, the sealant layer contains a saturated primary fattyacid amide having a melting point greater than 100° C. A “saturatedprimary fatty acid amide” is a molecule having the Structure (V):

wherein R¹ is a C₃ to C₂₇ alkyl moiety that is saturated. In anembodiment, R¹ is a C₁₁ to C₂₅, or a C₁₅ to C₂₃ alkyl moiety, or a C₁₅to C₂₁ alkyl moiety that is saturated. A “saturated” alky moiety is analkyl in which all carbon atoms are linked to one another via singlebonds (C—C bonds). In other words, a saturated alkyl moiety excludescarbon atoms linked via double bonds (C═C bonds). In an embodiment, R¹is selected from a C₁₇ alkyl moiety and a C₂₁ alkyl moiety that issaturated. Nonlimiting examples of suitable saturated primary fatty acidamides include behenamide, palmitamide, stearamide, and combinationsthereof.

In an embodiment, in the saturated primary fatty acid amide of theStructure (IV), R¹ is a C₂₁ alkyl moiety that is saturated. In a furtherembodiment, the saturated primary fatty acid amide is behenamide.Behenamide has the following Structure (VI):

In an embodiment, in the saturated primary fatty acid amide of theStructure (V), R¹ is a C₁₅ alkyl moiety that is saturated. In a furtherembodiment, the saturated primary fatty acid amide is palmitamide.

In an embodiment, in the saturated primary fatty acid amide of theStructure (V), R¹ is a C₁₇ alkyl moiety that is saturated. In a furtherembodiment, the saturated primary fatty acid amide is stearamide.

The saturated primary fatty acid amide has a melting point greater than100° C. In an embodiment, the saturated primary fatty acid amide has amelting point from greater than 100° C. to 150° C., or from 101° C., or102° C., or 103° C., or 104° C., or 105° C., or 106° C. to 113° C., or115° C., or 120° C., or 125° C., or 130° C., or 135° C., or 140° C., or145° C., or 150° C. In an embodiment, the saturated primary fatty acidamide is behenamide, which has a melting point of 108° C.-113° C. Inanother embodiment, the saturated primary fatty acid amide ispalmitamide, which has a melting point of 106° C.-107° C. In anotherembodiment, the saturated primary fatty acid amide is stearamide, whichhas a melting point of 109° C.

The sealant layer may contain more than one saturated primary fatty acidamide. In an embodiment, the sealant layer includes at least twosaturated primary fatty acid amides, wherein each saturated primaryfatty acid amide differs from one another compositionally, structurally,and/or physically.

In an embodiment, the sealant layer contains from 0.00047 wt % (4.7ppm), or 0.001 wt % (10 ppm), or 0.0025 wt % (25 ppm), or 0.0083 wt %(83 ppm), or 0.01 wt % (100 ppm), or 0.06 wt % (600 ppm) to 0.12 wt %(1200 ppm), or 0.18 wt % (1800 ppm), or 1.0 wt % (10000 ppm), or 1.25 wt% (12500 ppm), or 2.0 wt % (20000 ppm), or 3.0 wt % (30000 ppm), or 4.0wt % (40000 ppm), or 4.1 wt % (41000 ppm) saturated primary fatty acidamide, based on the total weight of the sealant layer.

The saturated primary fatty acid amide may comprise two or moreembodiments disclosed herein.

E. Optional Additive(s)

In an embodiment, the sealant layer includes one or more optionaladditives.

Nonlimiting examples of suitable additives include antiblock agents,antioxidants, antistatic agents, stabilizing agents, nucleating agents,colorants, pigments, ultra violet (UV) absorbers or stabilizers, flameretardants, compatibilizers, plasticizers, fillers, processing aids,antifog additive, crosslinking agents (e.g., peroxides), andcombinations thereof.

In an embodiment, the sealant layer includes an antiblock agent. An“antiblock agent” is a compound that minimizes, or prevents, blocking(i.e., adhesion) between two adjacent layers of film by creating amicroscopic roughening of the film layer surface, which reduces theavailable contact area between adjacent layers. The antiblock agent maybe organic or inorganic. Nonlimiting examples of suitable antiblockagents include silica, talc, calcium carbonate, and combinationsthereof. In an embodiment, the antiblock agent is silica (SiO₂). Thesilica may be organic silica or synthetic silica. In an embodiment, thesealant layer contains from 0 wt %, or 0.10 wt % (1000 ppm), or 0.20 wt% (2000 ppm), or 0.25 wt % (2500 ppm) to 0.3 wt % (3000 ppm), or 0.4 wt% (4000 ppm), or 0.5 wt % (5000 ppm), or 1.0 wt % (10000 ppm), or 1.5 wt% (15000 ppm), or 2.0 wt % (20000 ppm) antiblock agent, based on thetotal weight of the sealant layer.

In an embodiment, the sealant layer contains from 0 wt %, or 0.01 wt %,or 0.05 wt %, or 0.1 wt %, or 0.2 wt % to 0.3 wt %, or 0.4 wt %, or 0.5wt %, or 1.0 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 5.0 wt %additive, based on the total weight of the sealant layer.

The additive may comprise two or more embodiments disclosed herein.

In an embodiment, the sealant layer contains from 0.01 wt %, or 0.02 wt%, or 0.03 wt %, or 0.04 wt %, or 0.05 wt %, or 0.06 wt %, or 0.07 wt %,or 0.08 wt %, or 0.09 wt %, or 0.10 wt % to 0.15 wt %, or 0.20 wt %, or0.25 wt %, or 0.30 wt %, or 0.35 wt %, or 0.40 wt %, or 0.45 wt %, or0.50 wt %, or 0.80 wt %, or 1.0 wt %, or 1.5 wt %, or 2.0 wt %, or 2.5wt %, or 3.0 wt %, or 3.5 wt %, or 4.0 wt %, or 4.5 wt %, or 5.0 wt % ofa combined amount of the unsaturated primary fatty acid amide and thediprotic fatty acid, based on the total weight of the sealant layer.

In an embodiment, the unsaturated primary fatty acid amide and thediprotic fatty acid have a weight ratio of from 0.05:1, or 0.5:1, or1:1, or 1.4:1 to 2.9:1, or 3:1, or 5:1, or 10:1, or 15:1, or 20:1.

In an embodiment, the unsaturated primary fatty acid amide and thediprotic fatty acid have a molar ratio of from 1:1 to 1:2.

In an embodiment, the sealant layer has a Pre-Lamination COF from 0.01,or 0.05, or 0.10 to 0.18, or 0.20, or 0.21, or 0.25, or 0.27, or 0.30.

In an embodiment, the sealant layer has a thickness from 5 μm, or 8 μm,or 10 μm, or 15 μm, or 20 μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or45 μm, or 50 μm to 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80μm, or 90 μm, or 100 μm, or 120 μm, or 150 μm.

The sealant layer may comprise two or more embodiments disclosed herein.

2. Second Layer

The multilayer film includes a second layer. The second layer contains asecond ethylene-based polymer.

The second layer has two opposing surfaces. In an embodiment, the secondlayer is a continuous layer with two opposing surfaces.

The second layer is in contact with the sealant layer. The second layermay be in direct contact or in indirect contact with the sealant layer.In an embodiment, the second layer directly contacts the sealant layer.The term “directly contacts,” as used herein, is a layer configurationwhereby the second layer is located immediately adjacent to the sealantlayer and no intervening layers, or no intervening structures, arepresent between the sealant layer and the second layer.

In another embodiment, the second layer indirectly contacts the sealantlayer. The term “indirectly contacts,” as used herein, is a layerconfiguration whereby an intervening layer, or an intervening structure,is present between the sealant layer and the second layer.

The second ethylene-based polymer may be any ethylene-based polymerdisclosed herein. The second ethylene-based polymer may be the same ordifferent than the ethylene-based polymer of the sealant layer. In anembodiment, the second ethylene-based polymer is the same as theethylene-based polymer of the sealant layer. In another embodiment, thesecond ethylene-based polymer is different than the ethylene-basedpolymer of the sealant layer.

In an embodiment, the second ethylene-based polymer is a LLDPE, a LDPE,or a combination thereof. In a further embodiment, the LLDPE is anethylene/1-octene copolymer. In an embodiment, the second layer containsfrom 5 wt %, or 10 wt %, or 20 wt %, or 30 wt %, or 40 wt %, or 50 wt %,or 60 wt %, or 70 wt %, or 80 wt % to 90 wt %, or 95 wt %, or 99 wt %LLDPE; and a reciprocal amount of LDPE, or from 1 wt %, or 5 wt %, or 10wt %, or 20 wt % to 30 wt %, or 40 wt %, or 50 wt %, or 60 wt %, or 70wt %, or 80 wt %, or 90 wt %, or 95 wt % LDPE, based on the total weightof the second layer.

In an embodiment, the second layer contains one or more optionaladditives. The additive may be any additive disclosed herein. In anembodiment, the second layer contains from 0 wt %, or 0.01 wt %, or 0.05wt %, or 0.1 wt %, or 0.2 wt % to 0.3 wt %, or 0.4 wt %, or 0.5 wt %, or1.0 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 5.0 wt % additive,based on the total weight of the second layer.

In an embodiment, the second layer has a thickness from 5 μm, or 8 μm,or 10 μm, or 15 μm to 20 μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or45 μm, or 50 μm, or 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80μm, or 85 μm, or 90 μm, or 100 μm, or 120 μm, or 150 μm.

The second layer may be a substrate layer or a core layer. In anembodiment, the second layer is a core layer. A “core layer” is a layerof a film structure that is an inner layer. In other words, neithersurface of a core layer is an outermost surface of the film. In anembodiment, the second layer is a substrate layer. A “substrate layer”is a layer of a film structure that may be an inner layer or a skinlayer. A “skin layer” is an outermost layer of a film structure. Inother words, at least one surface of a skin layer is an outermostsurface of the film.

The second layer may comprise two or more embodiments disclosed herein.

3. Optional Third Layer

In an embodiment, the multilayer film includes an optional third layer.The third layer contains a third ethylene-based polymer.

The third layer has two opposing surfaces. In an embodiment, the thirdlayer is a continuous layer with two opposing surfaces.

The third layer is in contact with the second layer. The third layer maybe in direct contact or in indirect contact with the second layer. In anembodiment, the third layer directly contacts the second layer. Inanother embodiment, the third layer indirectly contacts the secondlayer.

The third ethylene-based polymer may be any ethylene-based polymerdisclosed herein. The third ethylene-based polymer may be the same ordifferent than the first ethylene-based polymer of the sealant layer,and the third ethylene-based polymer may be the same or different thanthe second ethylene-based polymer of the second layer. In an embodiment,the third ethylene-based polymer is the same as the secondethylene-based polymer of the second layer. In another embodiment, thethird ethylene-based polymer is different than the second ethylene-basedpolymer of the second layer.

In an embodiment, the third ethylene-based polymer is a LLDPE, a LDPE,or a combination thereof. In an embodiment, the third layer containsfrom 5 wt %, or 10 wt %, or 20 wt %, or 30 wt %, or 40 wt %, or 50 wt %,or 60 wt %, or 70 wt %, or 80 wt % to 90 wt %, or 99 wt % LLDPE; and areciprocal amount of LDPE, or from 1 wt %, or 10 wt %, or 20 wt % to 30wt %, or 40 wt %, or 50 wt %, or 60 wt %, or 70 wt %, or 80 wt %, or 90wt %, or 95 wt % LDPE, based on the total weight of the third layer.

In an embodiment, the third layer contains one or more optionaladditives. The additive may be any additive disclosed herein. In anembodiment, the third layer contains from 0 wt %, or 0.01 wt %, or 0.05wt %, or 0.1 wt %, or 0.2 wt % to 0.3 wt %, or 0.4 wt %, or 0.5 wt %, or1.0 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 5.0 wt % additive,based on the total weight of the third layer.

In an embodiment, the third layer has a thickness from 5 μm, or 8 μm, or10 μm, or 15 μm to 20 μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or 45μm, or 50 μm, or 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80μm, or 85 μm, or 90 μm, or 100 μm, or 120 μm, or 150 μm.

The third layer may be a substrate layer or a core layer. In anotherembodiment, the third layer is a substrate layer.

The third layer may comprise two or more embodiments disclosed herein.

In an embodiment, the multilayer film has the following Structure (VII):

sealant layer/second layer  Structure(VII).

In an embodiment, the sealant layer and the third layer are skin layerson opposing sides of the second layer, which is a core layer. In afurther embodiment, the sealant layer is in direct contact with thesecond layer, and the second layer is in direct contact with the thirdlayer. In an embodiment, the multilayer film has the following Structure(VIII):

sealant layer/second layer/third layer  Structure(VIII).

In an embodiment, the multilayer film consists essentially of, orconsists of, the sealant layer and the second layer. In anotherembodiment, the multilayer film consists essentially of, or consists of,the sealant layer, the second layer, and the third layer.

In an embodiment, the multilayer film has a thickness from 15 μm, or 20μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or 45 μm, or 50 μm, or 55 μmto 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80 μm, or 85 μm, or 90 μm, or95 μm, or 100 μm, or 150 μm, or 200 μm, or 250 μm, or 300 μm.

In an embodiment, the coextruded multilayer film contains, consistsessentially of, or consists of:

(1) a sealant layer containing, consisting essentially of, or consistingof:

(A) from 70 wt %, or 75 wt %, or 80 wt %, or 85 wt %, or 90 wt % to 93wt %, or 94 wt %, or 95 wt %, or 98 wt %, or 99 wt %, or 99.5 wt %, or99.99 wt % of the first ethylene-based polymer (such as

-   -   LLDPE and/or LDPE), based on the total weight of the sealant        layer, the first ethylene-based polymer having

(i) a density from 0.865 g/cc to 0.930 g/cc, or from 0.900 g/cc, or0.910 g/cc, or 0.915 g/cc to 0.920 g/cc, or 0.925 g/cc, or 0.930 g/cc;and

-   -   (ii) a melt index from 0.5 g/10 min to 25 g/10 min, or from 0.5        g/10 min, or 1.0 g/10 min to 1.5 g/10 min, or 2.0 g/10 min, or        3.0 g/10 min, or 4.0 g/10 min, or 5.0 g/10 min, or 8.0 g/10 min;

(B) from 0.00047 wt %, or 0.001 wt %, or 0.0095 wt %, or 0.01 wt %, or0.05 wt % to 0.08 wt %, or 0.10 wt %, or 0.20 wt %, or 0.24 wt %, or 0.5wt %, or 1.0 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 4.5 wt %,or 4.76 wt % unsaturated primary fatty acid amide (such as erucamideand/or oleamide), based on the total weight of the sealant layer, theunsaturated primary fatty acid amide having a melting point from 65° C.,or 70° C., or 75° C. to 80° C., or 85° C., or 90° C., or 95° C.;

(C) from 0.00047 wt %, or 0.001 wt %, or 0.0095 wt %, or 0.01 wt %, or0.02 wt % to 0.05 wt %, or 0.10 wt %, or 0.20 wt %, or 0.24 wt %, or 0.5wt %, or 1.0 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 4.5 wt %,or 4.76 wt % diprotic fatty acid (such as succinic acid), based on thetotal weight of the sealant layer, the diprotic fatty acid having

-   -   (i) a melting point greater from 101° C., 110° C., or 130° C.,        or 150° C., or 170° C., or 180° C. to 185° C., or 190° C., or        200° C., or 210° C., or 220° C., or 230° C., or 240° C.;        and (ii) a decomposition temperature from 220° C., or 225° C.,        or 230° C., or 235° C. to 240° C., or 245° C., or 250° C., or        270° C., or 300° C., or 310° C., or 320° C., or 330° C., or 340°        C., or 350° C.;

(D) optionally, from 0.00047 wt %, or 0.001 wt %, or 0.0025 wt %, or0.0083 wt %, or 0.01 wt %, or 0.06 wt % to 0.12 wt %, or 0.18 wt %, or1.0 wt %, or 1.25 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 4.1 wt% saturated primary fatty acid amide (such as behenamide), based on thetotal weight of the sealant layer, the saturated primary fatty acidamide having a melting point from 101° C., or 103° C., or 106° C. to113° C., or 115° C., or 120° C., or 125° C., or 130° C., or 135° C., or140° C.;

(E) optionally, from 0 wt %, or 0.01 wt %, or 0.05 wt %, or 0.1 wt %, or0.2 wt % to 0.3 wt %, or 0.4 wt %, or 0.5 wt %, or 1.0 wt %, or 2.0 wt%, or 3.0 wt %, or 4.0 wt %, or 5.0 wt % additive (such as an antiblockagent), based on the total weight of the sealant layer;

(2) a second layer in contact with the sealant layer, the second layercontaining a second ethylene-based polymer (such as LLDPE, LDPE, or acombination thereof); and(3) optionally, a third layer in contact with the second layer, thethird layer containing a third ethylene-based polymer (such as LLDPE,LDPE, or a combination thereof); and the coextruded multilayer film hasone, some, or all of the following properties:

(i) the sealant layer has a thickness from 5 μm, or 8 μm, or 10 μm, or15 μm, or 20 μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or 45 μm, or 50μm to 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80 μm, or 85 μm,or 90 μm, or 100 μm, or 120 μm, or 150 μm; and/or

(ii) the sealant layer contains from 0.01 wt %, or 0.02 wt %, or 0.03 wt%, or 0.04 wt %, or 0.05 wt %, or 0.06 wt %, or 0.07 wt %, or 0.08 wt %,or 0.09 wt %, or 0.10 wt % to 0.15 wt %, or 0.20 wt %, or 0.25 wt %, or0.30 wt % of a combined amount of the unsaturated primary fatty acidamide and the diprotic fatty acid, based on the total weight of thesealant layer; and/or

(iii) the sealant layer has a Pre-Lamination COF from 0.01, or 0.05, or0.10 to 0.18, or 0.20, or 0.21, or 0.25, or 0.27, or 0.30; and/or

(iv) the second layer has a thickness from 5 μm, or 8 μm, or 10 μm, or15 μm to 20 μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or 45 μm, or 50μm, or 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80 μm, or 85μm, or 90 μm, or 100 μm, or 120 μm, or 150 μm; and/or

(v) the third layer has a thickness from 5 μm, or 8 μm, or 10 μm, or 15μm to 20 μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or 45 μm, or 50 μm,or 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80 μm, or 85 μm, or90 μm, or 100 μm, or 120 μm, or 150 μm; and/or

(vi) the coextruded multilayer film has a thickness of from 15 μm, or 20μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or 45 μm, or 50 μm, or 55 μmto 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80 μm, or 85 μm, or 90 μm, or95 μm, or 100 μm, or 150 μm, or 200 μm, or 250 μm, or 300 μm; and/or

(vii) the unsaturated primary fatty acid amide and the diprotic fattyacid have a weight ratio of from 0.05:1, or 0.5:1, or 1:1, or 1.4:1 to2.9:1, or 3:1, or 5:1, or 10:1, or 15:1, or 20:1; and/or

(viii) the unsaturated primary fatty acid amide and the diprotic fattyacid have a molar ratio of from 1:1 to 1:2.

It is understood that the sum of the components in each of the layersdisclosed herein, including the foregoing layers, yields 100 weightpercent (wt %), based on the total weight of each respective layer.

In an embodiment, the coextruded multilayer film excludes non-migratoryslip agents, such as silicone.

Some methods, for example, used to construct films are by castcoextrusion or blown coextrusion methods. Combinations of these methodsare also possible. In an embodiment, the multilayer film is a coextrudedblown film.

The coextruded multilayer film may or may not be oriented. In anembodiment, the coextruded multilayer film is not an oriented film. In afurther embodiment, the coextruded multilayer film is not biaxiallyoriented. In other words, the coextruded multilayer film is notstretched after extrusion. In another embodiment, the coextrudedmultilayer film is oriented (e.g., biaxially oriented).

In an embodiment, the coextruded multilayer film is included in alaminate. In such embodiments, an outermost surface of the sealant layeris an outermost surface of the laminate.

The coextruded multilayer film may comprise two or more embodimentsdisclosed herein.

Laminate

The present disclosure provides a laminate. In an embodiment, thelaminate includes a first film containing a sealant layer and a secondfilm, wherein the first film is laminated to the second film. Thesealant layer contains (A) a first ethylene-based polymer having adensity from 0.865 g/cc to 0.930 g/cc and a melt index from 0.5 g/10 minto 25 g/10 min; (B) an unsaturated primary fatty acid amide having amelting point of 100° C. or less; and (C) a diprotic fatty acid having amelting point greater than 100° C. and a decomposition temperaturegreater than 200° C.

The laminate contains at least two films, or more than two films. Forexample, the laminate can have two, three, four, five, six, seven,eight, nine, ten, eleven, or more films. In an embodiment, the laminatecontains only two films, or only three films.

In an embodiment, the laminate has the following Structure (IX):

first film/second film  Structure(IX).

In an embodiment, the laminate includes a first film, an adhesive layerin contact with the first film, and a second film in contact with theadhesive layer. In an embodiment, the laminate has the followingStructure (X):

first film/adhesive layer/second film  Structure (X)

In an embodiment, the first film is a monolayer film containing asealant layer and the second film is a monolayer film containing asubstrate layer, and the laminate has the following Structure (XI):

sealant layer/adhesive layer/substrate layer  Structure(XI).

In an embodiment, the laminate includes an optional third film laminatedto the second film. In a further embodiment, the laminate includes anoptional second adhesive layer in contact with the second film, and anoptional third film in contact with the second adhesive layer. In anembodiment, the laminate has the following Structure (XII):

first film/adhesive layer/second film/second adhesive layer/thirdfilm  Structure (XII).

1. First Film

The laminate includes a first film. The first film includes a sealantlayer.

The first film has two opposing surfaces. The first film may be amonolayer film or a multilayer film. In an embodiment, the first film isa multilayer film containing at least two layers, or more than twolayers. For example, the first film can have two, three, four, five,six, seven, eight, nine, ten, or more layers. In an embodiment, thefirst film contains only one layer, or only three layers.

In an embodiment, the first film is a multilayer film including anoptional core layer in contact with the sealant layer and an optionalthird substrate layer in contact with the core layer. In an embodiment,the outermost surface of the third substrate is laminated to anoutermost surface of the second film.

A. Sealant Layer

The first film contains a sealant layer. The sealant layer may be anysealant layer disclosed herein. In an embodiment, the sealant layer is askin layer. In other words, an outermost surface of the sealant layer isan outermost surface of the first film, and further an outermost surfaceof the laminate.

B. Optional Core Layer and Optional Third Substrate Layer

In an embodiment, the first film is a multilayer film that includes acore layer and a third substrate layer.

The core layer has two opposing surfaces. In an embodiment, the corelayer is a continuous layer with two opposing surfaces. The core layeris in contact with the sealant layer. The core layer may be in directcontact or in indirect contact with the sealant layer. In an embodiment,the core layer directly contacts the sealant layer. In anotherembodiment, the core layer indirectly contacts the sealant layer.

In an embodiment, the core layer contains a third ethylene-basedpolymer. The third ethylene-based polymer may be any ethylene-basedpolymer disclosed herein. The third ethylene-based polymer may be thesame or different than the ethylene-based polymer of the sealant layer.In an embodiment, the third ethylene-based polymer is a LLDPE, a LDPE,or a combination thereof. In an embodiment, the core layer contains from5 wt %, or 10 wt %, or 20 wt %, or 30 wt %, or 40 wt %, or 50 wt %, or60 wt %, or 70 wt %, or 80 wt % to 90 wt %, or 95 wt %, or 99 wt %LLDPE; and a reciprocal amount of LDPE, or from 1 wt %, or 5 wt %, or 10wt %, or 20 wt % to 30 wt %, or 40 wt %, or 50 wt %, or 60 wt %, or 70wt %, or 80 wt %, or 90 wt %, or 95 wt % LDPE, based on the total weightof the core layer.

In an embodiment, the core layer contains one or more optionaladditives. The additive may be any additive disclosed herein. In anembodiment, the core layer contains from 0 wt %, or 0.01 wt %, or 0.05wt %, or 0.1 wt %, or 0.2 wt % to 0.3 wt %, or 0.4 wt %, or 0.5 wt %, or1.0 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 5.0 wt % additive,based on the total weight of the core layer. In an embodiment, the corelayer contains an additive that is a slip agent selected from anunsaturated primary fatty acid amide having a melting point of 100° C.or less; a saturated primary fatty acid amide having a melting pointgreater than 100° C.; a diprotic fatty acid having a melting pointgreater than 100° C. and a decomposition temperature greater than 200°C.; and combinations thereof.

In an embodiment, the core layer has a thickness from 5 μm, or 8 μm, or10 μm, or 15 μm to 20 μm, or 25 μm, or 30 μm, or 35 μm, or 40 μm, or 45μm, or 50 μm, or 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75 μm, or 80μm, or 85 μm, or 90 μm, or 100 μm, or 120 μm, or 150 μm.

The third substrate layer has two opposing surfaces. In an embodiment,the third substrate layer is a continuous layer with two opposingsurfaces. The third substrate layer is in contact with the core layerand the second film. The third substrate layer may be in direct contactor in indirect contact with the core layer. In an embodiment, the thirdsubstrate layer directly contacts the core layer. In another embodiment,the third substrate layer indirectly contacts the core layer. The thirdsubstrate layer may be in direct contact or in indirect contact with thesecond film. In an embodiment, the third substrate layer directlycontacts the second film. In another embodiment, the third substratelayer indirectly contacts the second film.

In an embodiment, the third substrate layer contains a fourthethylene-based polymer. The fourth ethylene-based polymer may be anyethylene-based polymer disclosed herein. The fourth ethylene-basedpolymer may be the same or different than the ethylene-based polymer ofthe sealant layer, and the fourth ethylene-based polymer may be the sameor different than the third ethylene-based polymer of the core layer. Inan embodiment, the fourth ethylene-based polymer is a LLDPE, a LDPE, ora combination thereof. In an embodiment, the third substrate layercontains from 5 wt %, or 10 wt %, or 20 wt %, or 30 wt %, or 40 wt %, or50 wt %, or 60 wt %, or 70 wt %, or 80 wt % to 90 wt %, or 95 wt %, or99 wt % LLDPE; and a reciprocal amount of LDPE, or from 1 wt %, or 5 wt%, or 10 wt %, or 20 wt % to 30 wt %, or 40 wt %, or 50 wt %, or 60 wt%, or 70 wt %, or 80 wt %, or 90 wt %, or 95 wt % LDPE, based on thetotal weight of the third substrate layer.

In an embodiment, the third substrate layer contains one or moreoptional additives. The additive may be any additive disclosed herein.In an embodiment, the core layer contains from 0 wt %, or 0.01 wt %, or0.05 wt %, or 0.1 wt %, or 0.2 wt % to 0.3 wt %, or 0.4 wt %, or 0.5 wt%, or 1.0 wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 5.0 wt %additive, based on the total weight of the third substrate layer.

In an embodiment, the third substrate layer has a thickness from 5 μm,or 8 μm, or 10 μm, or 15 μm to 20 μm, or 25 μm, or 30 μm, or 35 μm, or40 μm, or 45 μm, or 50 μm, or 55 μm, or 60 μm, or 65 μm, or 70 μm, or 75μm, or 80 μm, or 85 μm, or 90 μm, or 100 μm, or 120 μm, or 150 μm.

In an embodiment, the third substrate layer is corona treated.

The core layer and the third substrate layer may comprise two or moreembodiments disclosed herein.

The first film may comprise two or more embodiments disclosed herein.

2. Second Film

The laminate includes a second film. The first film is laminated to thesecond film.

The second film has two opposing surfaces. The second film may be amonolayer film or a multilayer film. In an embodiment, the second filmis a monolayer film. In another embodiment, the second film is amultilayer film containing at least two layers, or more than two layers.For example, the second film can have two, three, four, five, six,seven, eight, nine, ten, or more layers. In an embodiment, the secondfilm contains only one layer, or only two layers, or only three layers.

In an embodiment, the second film includes a substrate layer. Thesubstrate layer has two opposing surfaces. In an embodiment, thesubstrate layer is a continuous layer with two opposing surfaces.

The substrate layer is in contact with the first film. The substratelayer may be in direct contact or in indirect contact with the firstfilm. In an embodiment, the substrate layer directly contacts the firstfilm. In another embodiment, the substrate layer indirectly contacts thefirst film.

In an embodiment, the substrate layer is in contact with an optionaladhesive layer. The substrate layer may be in direct contact or inindirect contact with the adhesive layer. In an embodiment, thesubstrate layer directly contacts the adhesive layer. In anotherembodiment, the substrate layer indirectly contacts the adhesive layer.

In an embodiment, the substrate layer contains a component selected froma second ethylene-based polymer, propylene-based polymer, polyamide(such as nylon), polyester, ethylene vinyl alcohol copolymer,polyethylene terephthalate (PET), ethylene vinyl acrylate copolymer,ethylene methyl acrylate copolymer, ethylene ethyl acrylate copolymer,ethylene butyl acrylate copolymer, ethylene acrylic acid copolymer,ethylene methacrylic acid copolymer, an ionomer of ethylene acrylicacid, an ionomer of methacylic acid, maleic anhydride graftedethylene-based polymer, a polystyrene, a metal foil, and combinationsthereof. In an embodiment, the substrate layer contains PET. In anotherembodiment, the substrate layer contains a second ethylene-basedpolymer. The second ethylene-based polymer may be any ethylene-basedpolymer disclosed herein. The second ethylene-based polymer may be thesame or different than the ethylene-based polymer of the sealant layer.

In an embodiment, the second film, or further the substrate layer, has athickness from 5 μm, or 8 μm, or 10 μm, or 12 μm, or 15 μm to 20 μm, or25 μm, or 30 μm, or 35 μm, or 40 μm, or 45 μm, or 50 μm, or 55 μm, or 60μm, or 65 μm, or 70 μm, or 75 μm, or 80 μm, or 85 μm, or 90 μm, or 100μm, or 150 μm.

The substrate layer may comprise two or more embodiments disclosedherein.

The second film may comprise two or more embodiments disclosed herein.

3. Optional Adhesive Layer

In an embodiment, the laminate includes an adhesive layer. The adhesivelayer is in contact with the first film and the second film.

The adhesive layer has two opposing surfaces. In an embodiment, theadhesive layer is a continuous layer with two opposing surfaces. Theadhesive layer is in contact with the first film. The adhesive layer maybe in direct contact or in indirect contact with the first film. In anembodiment, the adhesive layer directly contacts the first film. Inanother embodiment, the adhesive layer indirectly contacts the firstfilm.

The adhesive layer contains an adhesive. Nonlimiting examples ofsuitable adhesives include polyurethane adhesives, polyacrylateadhesives, and combinations thereof. A nonlimiting example of a suitablepolyurethane adhesive is MOR-FREE™ 706A/C-79, a solvent-lesspolyurethane adhesive available from Rohm and Haas. A nonlimitingexample of a suitable polyacrylate adhesive is ROBOND™ L-168/CR3A, awater-based polyacrylate adhesive available from The Dow ChemicalCompany.

In an embodiment, the adhesive layer has a dry coating weight of from0.5 grams per square meter (g/m²), or 1.0 g/m², or 1.5 g/m², or 1.8g/m², or 1.9 g/m² to 2.0 g/m², or 2.5 g/m², or 3.0 g/m².

The adhesive layer may comprise two or more embodiments disclosedherein.

4. Optional Third Film

In an embodiment, the laminate includes a third film. The third film islaminated to the second film.

The third film has two opposing surfaces. The third film may be amonolayer film or a multilayer film. In an embodiment, the third film isa monolayer film. In another embodiment, the third film is a multilayerfilm containing at least two layers, or more than two layers. Forexample, the third film can have two, three, four, five, six, seven,eight, nine, ten, or more layers. In an embodiment, the third filmcontains only one layer, or only two layers, or only three layers.

In an embodiment, the third film includes a second substrate layer. Thesecond substrate layer may be any substrate layer disclosed herein.

The second substrate layer is in contact with the second film. Thesecond substrate layer may be in direct contact or in indirect contactwith the second film. In an embodiment, the second substrate layerdirectly contacts the second film. In another embodiment, the secondsubstrate layer indirectly contacts the second film.

The second substrate layer may comprise two or more embodimentsdisclosed herein.

The third film may comprise two or more embodiments disclosed herein

5. Optional Second Adhesive Layer

In an embodiment, the laminate includes a second adhesive layer. Thesecond adhesive layer is in contact with the second film. The secondadhesive layer may be any adhesive layer disclosed herein.

The second adhesive layer has two opposing surfaces. In an embodiment,the second adhesive layer is a continuous layer with two opposingsurfaces. The second adhesive layer is in contact with the second film.The second adhesive layer may be in direct contact or in indirectcontact with the second film. In an embodiment, the second adhesivelayer directly contacts the second film. In another embodiment, thesecond adhesive layer indirectly contacts the second film.

In an embodiment, the second adhesive layer is in contact with theoptional third film. The second adhesive layer may be in direct contactor in indirect contact with the third film. In an embodiment, the secondadhesive layer directly contacts the third film. In another embodiment,the second adhesive layer indirectly contacts the third film.

The second adhesive layer may comprise two or more embodiments disclosedherein

In an embodiment, the first film is a multilayer film with a sealantlayer, a core layer, and a third substrate layer; and the second film isa monolayer film containing a substrate layer; and the laminate has thefollowing Structure (XIII):

sealant layer/core layer/third substrate layer/adhesive layer/substratelayer  Structure(XIII).

In an embodiment, the first film is a multilayer film with a sealantlayer, a core layer, and a third substrate layer; and the second film isa monolayer film containing a substrate layer; the third film is amonolayer film containing a second substrate layer; and the laminate hasthe following Structure (XIV): sealant layer/core layer/third substratelayer/adhesive layer/substrate layer/second

adhesive layer/second substrate layer  Structure(XIV).

In an embodiment, the sealant layer of the laminate has a Pre-LaminationCOF from 0.01, or 0.05, or 0.10 to 0.18, or 0.20, or 0.21, or 0.25, or0.27, or 0.30.

In an embodiment, the sealant layer of the laminate has a COF of from0.01, or 0.05, or 0.10 to 0.18, or 0.20, or 0.21, or 0.25, or 0.27, or0.30 after curing at 60° C. for 60 hours (hereinafter, the “LaminateCOF”). In an embodiment, the sealant layer of the laminate has a changein COF after 60° C. cure of less than 0.20, or less than 0.15, or lessthan 0.10. In another embodiment, the sealant layer of the laminate hasa change in COF from −0.20, or −0.10, or −0.05, or −0.02, or 0 to 0.01,or 0.05, or 0.10, or 0.15, or less than 20. The change in COF iscalculated in accordance with the following Equation (I):

COF Change=Laminate COF−Pre-Lamination COF  Equation (I).

In an embodiment, the laminate contains, consists essentially of, orconsists of:

(1) a first film containing

(A) a sealant layer containing, consisting essentially of, or consistingof:

-   -   (i) from 70 wt %, or 75 wt %, or 80 wt %, or 85 wt %, or 90 wt %        to 93 wt %, or 94 wt %, or 95 wt %, or 98 wt %, or 99 wt %, or        99.5 wt %, or 99.99 wt % of a first ethylene-based polymer (such        as LLDPE and/or LDPE), based on the total weight of the sealant        layer, the ethylene-based polymer having (a) a density from        0.865 g/cc to 0.930 g/cc, or from 0.900 g/cc, or 0.910 g/cc, or        0.915 g/cc to 0.920 g/cc, or 0.925 g/cc, or 0.930 g/cc; and (b)        a melt index from 0.5 g/10 min to 25 g/10 min, or from 0.5 g/10        min, or 1.0 g/10 min to 1.5 g/10 min, or 2.0 g/10 min, or 3.0        g/10 min, or 4.0 g/10 min, or 5.0 g/10 min, or 8.0 g/10 min;    -   (ii) from 0.00047 wt %, or 0.001 wt %, or 0.0095 wt %, or 0.01        wt %, or 0.05 wt % to 0.08 wt %, or 0.10 wt %, or 0.20 wt %        unsaturated primary fatty acid amide (such as erucamide and/or        oleamide), based on the total weight of the sealant layer, the        unsaturated primary fatty acid amide having a melting point from        65° C., or 70° C., or 75° C. to 80° C., or 85° C., or 90° C.;    -   (iii) from 0.00047 wt %, or 0.001 wt %, or 0.0095 wt %, or 0.01        wt %, or 0.02 wt % to 0.05 wt %, or 0.10 wt %, or 0.20 wt %        diprotic fatty acid (such as succinic acid), based on the total        weight of the sealant layer, the diprotic fatty acid having (a)        a melting point from 101° C., 110° C., or 130° C., or 150° C.,        or 170° C., or 180° C. to 185° C., or 190° C., or 200° C., or        210° C., or 220° C., or 230° C., or 240° C.; and (b) a        decomposition temperature from 220° C., or 225° C., or 230° C.,        or 235° C. to 240° C., or 245° C., or 250° C., or 270° C., or        300° C., or 310° C., or 320° C., or 330° C., or 340° C., or 350°        C.;    -   (iv) optionally, from 0.00047 wt %, or 0.001 wt %, or 0.0025 wt        %, or 0.0083 wt %, or 0.01 wt %, or 0.06 wt % to 0.12 wt %, or        0.18 wt %, or 1.0 wt %, or 1.25 wt %, or 2.0 wt % saturated        primary fatty acid amide (such as behenamide), based on the        total weight of the sealant layer, the saturated primary fatty        acid amide having a melting point from 101° C., or 103° C., or        106° C. to 113° C., or 115° C., or 120° C., or 125° C., or 130°        C., or 135° C., or 140° C.;    -   (v) optionally, from 0 wt %, or 0.01 wt %, or 0.05 wt %, or 0.1        wt %, or 0.2 wt % to 0.3 wt %, or 0.4 wt %, or 0.5 wt %, or 1.0        wt %, or 2.0 wt %, or 3.0 wt %, or 4.0 wt %, or 5.0 wt %        additive (such as an antiblock agent), based on the total weight        of the sealant layer;

(B) optionally, a core layer in contact with the sealant layer, the corelayer containing a third ethylene-based polymer (such as LLDPE and/orLDPE);

(C) optionally, a third substrate layer in contact with the core layer,the third substrate layer containing a fourth ethylene-based polymer(such as LLDPE and/or LDPE);

(2) optionally, an adhesive layer in contact with the first film;(3) a second film containing a substrate layer in contact with theadhesive layer, the substrate layer containing a component selected froma second ethylene-based polymer, a propylene-based polymer, a polyamide(such as nylon), a polyester, PET, a metal foil, and combinationsthereof; wherein the first film is laminated to the second film; and thelaminate has one, some, or all of the following properties:

(i) the sealant layer contains from 0.01 wt %, or 0.02 wt %, or 0.03 wt%, or 0.04 wt %, or 0.05 wt %, or 0.06 wt %, or 0.07 wt %, or 0.08 wt %,or 0.09 wt %, or 0.10 wt % to 0.15 wt %, or 0.20 wt %, or 0.25 wt %, or0.30 wt % of a combined amount of the unsaturated primary fatty acidamide and the diprotic fatty acid, based on the total weight of thesealant layer; and/or

(ii) the sealant layer has a Pre-Lamination COF from 0.01, or 0.05, or0.10 to 0.18, or 0.20, or 0.21, or 0.25, or 0.27, or 0.30; and/or

(iii) the sealant layer has a Laminate COF of from 0.01, or 0.05, or0.10 to 0.18, or 0.20, or 0.21, or 0.25, or 0.27, or 0.30; and/or

(iv) the sealant layer of the laminate has a change in COF of from−0.20, or −0.10, or −0.05, or −0.02, or 0 to 0.01, or 0.05, or 0.10, or0.15, or less than 20; and/or

(v) the laminate has a thickness of from 15 μm, or 20 μm, or 25 μm, or30 μm, or 35 μm, or 40 μm, or 45 μm, or 50 μm, or 55 μm to 60 μm, or 65μm, or 70 μm, or 75 μm, or 80 μm, or 85 μm, or 90 μm, or 95 μm, or 100μm, or 150 μm, or 200 μm, or 250 μm, or 300 μm; and/or

(vi) the unsaturated primary fatty acid amide and the diprotic fattyacid have a weight ratio of from 0.05:1, or 0.5:1, or 1:1, or 1.4:1 to2.9:1, or 3:1, or 5:1, or 10:1, or 15:1, or 20:1; and/or

(vii) the unsaturated primary fatty acid amide and the diprotic fattyacid have a molar ratio of from 1:1 to 1:2.

In an embodiment, the laminate excludes non-migratory slip agents, suchas silicone.

The first film, the second film, and the optional third film of thelaminate may be a coextruded multilayer structure.

Some methods, for example, used to construct laminates are by adhesivelamination, extrusion lamination, thermal lamination, dry lamination,and solvent-less lamination. Combinations of these methods are alsopossible.

The first film, the second film, and the optional third film of thelaminate may or may not be oriented. In an embodiment, one or more, oreach of the first film, the second film, and the optional third film isnot an oriented film. In a further embodiment, one or more, or each offirst film, the second film, and the optional third film is notbiaxially oriented. In another embodiment, one or more, or each of firstfilm, the second film, and the optional third film is oriented (e.g.,biaxially oriented).

The laminate may comprise two or more embodiments disclosed herein.

The present disclosure also provides an article containing thecoextruded multilayer film and/or the laminate, such as a package.Nonlimiting examples of suitable packages include food packages,specialty packages, and detergent packages (liquid and powder). In anembodiment, a package is provided, the package formed from two opposinglaminates. In an embodiment, the sealant layer of the first laminate isin contact with the sealant layer of the second laminate. In a furtherembodiment, a heat seal is formed from the opposing sealant layers toproduce a package.

By way of example, and not limitation, some embodiments of the presentdisclosure will now be described in detail in the following Examples.

Examples

Materials used in the examples are provided in Table 1 below.

TABLE 1 Material/Description Properties Source DOWLEX ™ 2045G MI(I2)(190° C./2.16 kg) = 1.0 g/10 min, The Dow Chemical(ethylene/1-octene copolymer)(LLDPE) Density = 0.920 g/cc, Melting point= 119° C. Company Erucamide 95% purity J&K Scientific Ltd. (unsaturatedprimary fatty acid amide) Melting point = 79° C. Succinic Acid 95%purity Meryer (Shanghai Mai (diprotic fatty acid) Melting point = 185°C. Ruier Chemical Decomposition Temperature = 235° C. Technology Co.,Ltd.

Monolayer Blown Film: A slip agent blend is prepared by blending theerucamide and succinic acid at a specific molar ratio. Then, the slipagent blend and DOWLEX™ 2045G are added to a Haake™ blown line extruder,and mixed at 190° C. for 10 minutes. Monolayer blown film samples arefabricated on the Haake™ blown line (die gap=1 mm; temperatureprofile=180-210° C.; length/diameter (L/D) ratio=25; output=5 kg/hour).The resulting monolayer blown film samples have a thickness of 50 μm.Two weeks after the monolayer blown film samples are formed, themonolayer blown film samples are tested for Pre-Lamination COF. Fivespecimens of each monolayer blown film are tested, and the averagePre-Lamination COF is reported. The results are reported in Table 2.

Laminate

The monolayer blown film samples prepared above undergo corona treatment(150 Volts) using a CTP 2000KA from Nanjing Suman Electronics Co. Ltd.

A PET substrate layer with a thickness of 12 μm is provided. The PETsubstrate layer has two opposing surfaces. One surface of the PETsubstrate layer is coated with ROBOND™ L-168/CR3A (a water-basedpolyacrylate adhesive from The Dow Chemical Company) using an AutomaticCoating Machine KY-1000 from Beijing Jingjing Technology Co. Ltd. (withan RDS coating rod to control thickness and a coating speed of 100mm/min). The coated PET substrate layer is placed in an oven at 80° C.for 40 seconds to dry the solvent of the ROBOND™ L-168/CR3A adhesive,forming an adhesive layer having a dry weight of 2 g/m². The PETsubstrate layer and adhesive layer have the following Structure (A):

PET substrate layer/adhesive layer  Structure (A).

The corona-treated monolayer blown film samples are laminated withStructure (A) via hot roller at 80° C. using a Beijing Century JintuSCI-TECH Co., Ltd. multi-function laminator (model HR-380). Then, thesamples are placed in an oven at 60° C. for 60 hours for aging. Thelayer formed by the corona-treated monolayer blown film samples is asealant layer. The resulting laminates have the following Structure (B):

PET substrate layer/adhesive layer/sealant layer   Structure (B).

The PET substrate layer is an outer layer that is in direct contact withthe adhesive layer, and the adhesive layer is in direct contact with thesealant layer. The resulting laminates have a thickness of 80 μm. Thelayer configurations are provided below in Table 2.

One week after aging, the laminate samples are tested for Laminate COF.Five specimens of each laminate are tested, and the average Laminate COFis reported. The results are reported in Table 2. In Table 2, “CS”refers to Comparative Sample.

Comparative Sample 4 is a corona-treated monolayer blown film (i.e., CS4 is not laminated). Laminate COF is not measured for Comparative Sample4 because it is not a laminate structure.

TABLE 2 Ex. 1⁶ Ex. 2⁶ CS 3⁶ CS 4⁷ Sealant Layer Composition¹ DOWLEX ™2045G (wt %)² 99.9 99.9 99.9 100 Erucamide (wt %)² 0.074 0.059 0.1 —Succinic Acid (wt %)² 0.026 0.041 — — Total wt %² 100 100 100 100Properties: Sealant Layer Molar Ratio of 1:1 1:2 N/A N/AErucamide:Succinic Acid Sealant Layer Weight Ratio of 2.86:1   1.43:1  N/A N/A Erucamide:Succinic Acid Pre-Lamination COF³ 0.20 ± 0.02 0.16 ±0.02 0.15 ± 0.02 0.32 ± 0.05 Laminate COF⁴ 0.18 ± 0.03 0.17 ± 0.03 0.35± 0.03 N/A COF Change⁵ −0.02 0.01 0.20 N/A ¹The sealant layer is formedfrom the monolayer blown film described above. ²Based on the totalweight of the sealant layer. ³Pre-Lamination COF is measured two weeksafter the monolayer blown film samples are formed, before the monolayerblown film samples are laminated. ⁴Laminate COF is measured after alaminate is formed, and one week after samples are aged in an oven at60° C. for 60 hours. ⁵COF Change is calculated in accordance with thefollowing equation: COF Change = Laminate COF − Pre-Lamination COF. ⁶Ex.1, Ex. 2 and CS 3 are laminate structures having Structure B (PETsubstrate layer/adhesive layer/sealant layer). ⁷CS 4 is a corona-treatedmonolayer blown film that is a sealant layer.

As shown, a comparative laminate with an adhesive layer, a PET substratelayer, and a sealant layer containing (A) an ethylene-based polymer(DOWLEX™ 2045G and LDPE) and (B) an unsaturated primary fatty acid amidehaving a melting point of 100° C. or less (erucamide) (CS 3)—and no (C)diprotic fatty acid having a melting point greater than 100° C. and adecomposition temperature greater than 200° C.—exhibits a high LaminateCOF of 0.35, and a high COF Change of 0.20.

Applicant surprisingly found that a laminate with an adhesive layer, aPET substrate layer, and a sealant layer containing (A) anethylene-based polymer (DOWLEX™ 2045G and LDPE); (B) an unsaturatedprimary fatty acid amide having a melting point of 100° C. or less(erucamide); and (C) diprotic fatty acid having a melting point greaterthan 100° C. and a decomposition temperature greater than 200° C.(succinic acid) (Ex. 1-2) advantageously exhibits a Pre-Lamination COFof less than 0.30, a Laminate COF of less than 0.30, and a COF Change of0.01 or less.

It is specifically intended that the present disclosure not be limitedto the embodiments and illustrations contained herein, but includemodified forms of those embodiments including portions of theembodiments and combinations of elements of different embodiments ascome within the scope of the following claims.

1. A coextruded multilayer film comprising at least two layerscomprising: a sealant layer comprising (A) a first ethylene-basedpolymer having a density from 0.865 g/cc to 0.930 g/cc and a melt indexfrom 0.5 g/10 min to 25 g/10 min; (B) an unsaturated primary fatty acidamide having a melting point of 100° C. or less; (C) a diprotic fattyacid having a melting point greater than 100° C. and a decompositiontemperature greater than 200° C.; and a second layer in contact with thesealant layer, the second layer comprising a second ethylene-basedpolymer.
 2. The coextruded multilayer film of claim 1, wherein theunsaturated primary fatty acid amide is selected from the groupconsisting of erucamide, oleamide, and combinations thereof.
 3. Thecoextruded multilayer film of claim 1, wherein the diprotic fatty acidis selected from the group consisting of succinic acid, hexanedioicacid, octanedioic acid, decanedioic acid, dodecanedioic acid, andcombinations thereof.
 4. The coextruded multilayer film of claim 1,wherein the first ethylene-based polymer is selected from the groupconsisting of an ethylene homopolymer, an ethylene/α-olefin copolymer,and combinations thereof.
 5. The coextruded multilayer film of claim 1,wherein the sealant layer further comprises a saturated primary fattyacid amide having a melting point greater than 100° C.
 6. The coextrudedmultilayer film of claim 1, wherein the sealant layer comprises from0.01 wt % to 5.0 wt % of a combined amount of the unsaturated primaryfatty acid amide and the diprotic fatty acid, based on the total weightof the sealant layer.
 7. A laminate comprising the coextruded multilayerfilm of claim
 1. 8. A laminate comprising: a first film comprising asealant layer comprising (A) a first ethylene-based polymer having adensity from 0.865 g/cc to 0.930 g/cc and a melt index from 0.5 g/10 minto 25 g/10 min; (B) an unsaturated primary fatty acid amide having amelting point of 100° C. or less; (C) a diprotic fatty acid having amelting point greater than 100° C. and a decomposition temperaturegreater than 200° C.; and a second film, wherein the first film islaminated to the second film.
 9. The laminate of claim 8, wherein theunsaturated primary fatty acid amide is selected from the groupconsisting of erucamide, oleamide, and combinations thereof.
 10. Thelaminate of claim 8, wherein the diprotic fatty acid is selected fromthe group consisting of succinic acid, hexanedioic acid, octanedioicacid, decanedioic acid, dodecanedioic acid, and combinations thereof.11. The laminate of claim 8, wherein the first ethylene-based polymer isselected from the group consisting of an ethylene homopolymer, anethylene/α-olefin copolymer, and combinations thereof.
 12. The laminateof claim 8, wherein the sealant layer further comprises a saturatedprimary fatty acid amide having a melting point greater than 100° C. 13.The laminate of claim 8, wherein the sealant layer has a LaminateCoefficient of Friction (COF) from 0.01 to 0.30.
 14. The laminate ofclaim 8, wherein the second film comprises a substrate layer comprisinga component selected from the group consisting of a secondethylene-based polymer, a propylene-based polymer, polyamide, polyester,ethylene vinyl alcohol copolymer, polyethylene terephthalate, ethylenevinyl acrylate copolymer, ethylene methyl acrylate copolymer, ethyleneethyl acrylate copolymer, ethylene butyl acrylate copolymer, ethyleneacrylic acid copolymer, ethylene methacrylic acid copolymer, an ionomerof ethylene acrylic acid, an ionomer of methacylic acid, maleicanhydride grafted ethylene-based polymer, a polystyrene, a metal foil,and combinations thereof.
 15. The laminate of claim 8, furthercomprising a third film, wherein the third film is laminated to thesecond film.